American Institute of Physics, Journal of Applied Physics, 21(121), p. 215108
DOI: 10.1063/1.4985172
Full text: Unavailable
Correlatively employing density functional theory and experiments congregated around high power pulsed magnetron sputtering, a plasma-surface model for metastable Cr0.8Al0.2N (space group Fm3¯m) is developed. This plasma-surface model relates plasma energetics with film composition, crystal structure, mass density, stress state, and elastic properties. It is predicted that N Frenkel pairs form during Cr0.8Al0.2N growth due to high-energy ion irradiation, yielding a mass density of 5.69 g cm−3 at room temperature and Young's modulus of 358–130 GPa in the temperature range of 50–700 K for the stress-free state and about 150 GPa larger values for the compressive stress of 4 GPa. Our measurements are consistent with the quantum mechanical predictions within 5% for the mass density and 3% for Young's modulus. The hypothesis of a stress-induced Young's modulus change may at least in part explain the spread in the reported elasticity data ranging from 250 to 420 GPa.