Copper sulfide is a promising p-type inorganic semiconductor for optoelectronic devices such as solar cells, due its small band gap energy and its electrical properties. In this work nanocrystalline copper sulfide (Cu_xS), with two stoichiometric ratios (x = 2, 1.8) was obtained by one-pot synthesis at 220, 230, 240 and 260 °C in an organic solvent and amorphous Cu_xS was obtained in aqueous solution. Nanoparticle-like nucleation centers are formed at lower temperatures (220 °C), mixtures of morphologies (nanorods, nanodisks and nanoprisms) are seen at 230 and 240 °C, in which the nanodisks are predominant, while big hexagonal/prismatic crystals are obtained at 260 °C according to TEM results. A mixture of chalcocite and digenite phases was found at 230 and 240 °C, while a clear transition to a pure digenite phase was seen at 260 °C. The evolution of morphology and transition of phases is consistent to the electrical, optical, and morphological properties of the copper sulfide. In fact, digenite Cu_1.8S is less resistive (346 Ω/sq) and has a lower energy band gap (1.6 eV) than chalcocite Cu₂S (5.72 × 10⁵ Ω/sq, 1.87 eV). Low resistivity was also obtained in Cu_xS synthesized in aqueous solution, despite its amorphous structure. All Cu_xS products could be promising for optoelectronic applications.