Wiley, Journal of Polymer Science Part A: Polymer Chemistry, 23(42), p. 5954-5963, 2004
DOI: 10.1002/pola.20428
Full text: Unavailable
A benzoxazine compound with a maleimide group, 3-phenyl-3,4-dihydro-2H-6-(N-maleimido)-1,3-benzoxazine (HPM-Ba), was prepared from N-(4-hydroxyphenyl)maleimide, formaldehyde, and aniline. The chemical structure of HBM-Ba was identified by FT-IR, 1H-NMR, and elemental analysis. HPM-Ba showed a melting point of 52-55 °C and good solubility in common organic solvents. HPM-Ba showed a two-stage process of thermal polymerization. The first stage arose from the polymerization of maleimide groups, and the second one was the ring-opening reaction of benzoxazine groups. Fusible polymaleimides with a Tg of around 100 °C could be obtained by thermally polymerizing HPM-Ba at 130 °C. Further polymerizing the polymaleimides at 240 °C resulted in a completely cured resin showing a Tg at 204 °C. Good thermal stability and self-extinguishing behavior was observed with the cured polybenzoxazine resins. ; JNL0004280