The versatility of perturbed angular correlations (PAC) in the study of nanostructures and thin films is demonstrated, namely for the specific cases of ZnO/Cd$_x$Zn$_{1-x}$O thin films and Ga$_2$O$_3$ powder pellets and nanowires, examples of transparent conductive oxides. PAC measurements as a function of annealing temperature were performed after implantation of $^{111m}$Cd$/^{111}$Cd (T$_{1/2}$=48$\,$min.) and later compared to density functional theory simulations. For ZnO, the substitution of Cd probes at Zn sites was observed, as well as the formation of a probe-defect complex. The ternary Cd$_x$Zn$_{1-x}$O (x=0.16) showed good macroscopic crystal quality but revealed some clustering of local defects around the probe Cd atoms, which could not be annealed. In the Ga$_2$O$_3$ samples, the substitution of the Cd probes in the octahedral Ga-site was observed, demonstrating the potential of ion-implantation for the doping of nanowires.