Copper and iron modified SBA-15 and SBA-16 materials were prepared by incipient wetness impregnation technique and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), N2 physisorption, temperature-programmed reduction (TPR-TGA), UV-Vis diffuse reflectance and Mössbauer spectroscopy. Formation of finely dispersed copper and iron-oxide species was observed on both supports, whereas copper ferrite could be evidenced only on SBA-15. It was found that the structural and surface properties of the mesoporous supports determine the type of formed metal oxides, their dispersion, reducibility and the catalytic activity in total oxidation of toluene. On SBA-16 support penetration of metal salt into the bimodal channel system is hindered therefore separate copper- and iron-oxide phases are formed on the outer surface of catalysts. The catalytic activity and stability are lower due to the easier agglomeration of particles. On SBA-15 support finely dispersed metal-oxides can be found in the mesoporous channels. Their interaction is favored to form bimetallic phases enhancing the catalytic activity and stability in total oxidation of toluene.