Elsevier, Journal of Hazardous Materials, 1-2(189), p. 384-390
DOI: 10.1016/j.jhazmat.2011.02.049
Full text: Download
A copper-nanoparticle-doped carbon was prepared from an alginate based precursor in a one step carbonisation-reduction procedure based on the modified polyol process. The ion exchange capacity of the precursor as well as the porosity, metal content, thermal properties, of the final product, were investigated. The preparation route leads to a porous carbon/copper composite with predefined metal loading reaching up to over 30% (w/w) of finely dispersed Cu nanoparticles of fairly uniform size. NO catalytic abatement evaluation showed high efficiency even at low temperatures compared to other recently reported carbon supported catalysts.