Electrochemical potentiodynamic polarization curves and immersion tests for 300 h at 700°C in a furnace have been used to evaluate the corrosion resistance of Fe-Si metallic coatings added with up to 50 wt.% of NiCrAIY. The corrosive environment was fuel oil ashes from a steam generator. The composition of fuel oil ashes includes high content of vanadium, sodium and sulfur. The results obtained show that only the addition of 20 wt.% NiCrAlY to the Fe-Si coating improves its corrosion resistance. The behavior of all tested coatings is explained by the results obtained from the analysis of every coating using electron microscopy and energy dispersive X-ray analysis.