Elsevier, Thin Solid Films, 19(515), p. 7658-7661
DOI: 10.1016/j.tsf.2006.11.138
Full text: Download
The piezoresistive property of n-type and p-type nanocrystalline silicon thin films deposited on plastic (PEN) at a substrate temperature of 150 °C by hot-wire chemical vapor deposition, is studied. The crystalline fraction decreased from 80% to 65% in p-type and from 84% to 62% in n-type films, as the dopant gas-to-silane flow rate ratio was increased from 0.18% to 3–3.5%. N-type films have negative gauge factor (− 11 to − 16) and p-type films have positive gauge factor (9 to 25). In n-type films the higher gauge factors (in absolute value) were obtained by increasing the doping level whereas in p-type films higher gauge factors were obtained by increasing the crystalline fraction.