A small concentration of Pb2+ ions is introduced into crystals of NaCl:Cd to monitor the aggregation and precipitation behavior of cadmium in NaCl. The evolution of the absorption and emission spectra of Pb2+ is followed during ageing and thermal annealing treatments. Moreover, the annihilation behavior of those spectra is correlated with that measured for the Raman peaks associated to Suzuki-phase precipitates. The main conclusion of this work is that Pb2+ becomes incorporated in the Suzuki-phase of Cd and gives rise to an absorption band at 274 nm and a corresponding emission band at 460 nm. On the other hand, absorption and luminescence bands occurring at 284 and 390 nm, respectively, are attributed to Pb2+ included in another precipitated phase. This phase develops at ageing temperatures <80°C and its structure is not definitely identified.Eine geringe Konzentration von Pb2+-Ionen wird in NaCl:Cd eingebracht, um die Zusammenlagerung und das Präzipitationsverhalten von Cd in NaCl zu verfolgen. Die Entwicklung der Absorptions- und Emissionsspektren von Pb2+ werden während der Alterung und thermischer Temperung registriert. Darüberhinaus wird das Annihilationsverhalten dieser Spektren mit denen korreliert, die für die mit den Suzuki-Phasen-Präzipitaten verknüpften Ramanmaxima gemessen werden. Die hauptsächliche Folgerung ist, daß Pb2+ in die Suzuki-Phase des Cd eingebaut wird und Anlaß zu einer Absorptionsbande bei 274 nm und einer entsprechenden Emissionsbande bei 460 nm gibt. Auf der anderen Seite werden die bei 284 und 390 nm auftretenden Absorptionsbzw. Lumineszenzbanden Pb2+ zugeordnet, das in einer anderen präzipitierten Phase eingeschlossen ist. Diese Phase entwickelt sich bei Alterungstemperaturen <80°C und ihre Struktur kann nicht eindeutig bestimmt werden.