In this work chromium-rich coatings impregnated with fullerene-like (IF)-WS₂ nanoparticles were deposited on stainless steel substrates. The coatings were obtained from a trivalent chromium bath at pH 2 by galvanostatic electrodeposition. Zinc and cobalt salts were added to the aqueous solution in small amounts serving as cationic growth promoters. Photodeposition of tin-palladium nanoparticles was used as seeding enhancer for the co-deposition of the fullerene-like nanoparticles. The coatings were characterized by a number of techniques and were found to show a decreasing gradient of the IF nanoparticles towards the film-substrate interface. Tribological tests showed that in contrast to the substrate and the pure metal coating, the IF-containing films exhibit low friction and wear.