Society of Photo-optical Instrumentation Engineers, Proceedings of SPIE, 2014
DOI: 10.1117/12.2043704
Full text: Download
Free-standing (0002)-oriented GaN substrates (φ = 2”) were coated with 200 nm of ZnO and used as templates for the growth of GaN thin films. SEM and AFM revealed that such GaN layers had a relatively homogenous surface morphology with an RMS roughness (5 µm x 5 µm) of less than 4nm. XRD studies revealed strained ZnO growth on the GaN substrate and the reproduction of the substrate rocking curve for the GaN overlayers after only a hundred nm of growth, thus indicating that the GaN films had superior crystallographic quality compared to those grown on sapphire or ZnO/sapphire substrates. Quarter-wafer areas of GaN were removed from the GaN substrate (by selective chemical etching away of the ZnO interlayer). The expensive GaN substrates were then reclaimed/reused (without the need for polishing) for a second cycle of ZnO and GaN growth, which gave similar XRD, SEM, CL and AFM results to the first cycle.