In the present work, the resonance Raman, UV-vis-NIR and scanning electron microscopic (SEM) data of nanorods (about approximately 300 nm in diameter) and nanofibers (about approximately 93 nm in diameter) of PANI are presented and compared. The PANI samples were synthesized in aqueous media with dodecybenzenesulfonic acid (DBSA) and beta-naphtalenesulfonic acid (beta-NSA) as dopants, respectively. The presence of bands at 578, 1400 and 1, 632 cm(-1) in the Raman spectra of PANI-NSA and PANI-DBSA shows that the formation of cross-linking structures is a general feature of the PANI chains prepared in micellar media. It is proposed that these structures are responsible for the one-dimensional PANI morphology formation. In addition, the Raman band at 609 cm(-1) of PANI fibers is correlated with the extended PANI chain conformation.