Elsevier, Physics Procedia, (8), p. 2-9, 2010
DOI: 10.1016/j.phpro.2010.10.002
Full text: Download
Polycrystalline samples of Gd0.8Sr0.2Fe0.8M0.2O3 (M=Cr, Ga) are prepared by combustion route and pore wetting technique in order to compare the influence of the morphology in the performance of two cathodes for Solid Oxide Fuel Cells. When polycarbonate membranes are used as templates nanowire arrays with a diameter of 50–70 nm are obtained. Comparing the results obtained by Electrochemical Impedance Spectroscopy (EIS) measurements, it is clearly observed that the cathodic resistance considerably decreases when optimized synthesis parameters are used, obtaining a better performance for the Gd0.8Sr0.2Fe0.8Ga0.2O3 nanowires with an area specific resistance (ASR) value at 850∘C of 0.195 Ω cm2.