Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) ; Processo FAPESP: 03/04097-7 ; Objectives. This study evaluated the effect of water-bath post-polymerization at 55 degrees C for 10 min (WB) on the content and leaching of residual compounds, degree of conversion, flexural strength, and hardness of hard chairside reline resins (Kooliner: K, New Truliner: N, Ufi Gel hard: U, and Tokuso Rebase Fast: T).Methods. Leaching experiments were made by storing specimens (n = 48) in artificial saliva at 37 +/- 1 degrees C and analyzing residual monomers and plasticizer by HPLC. Analysis of residual monomer and plasticizer content (n = 48) was also made by HPLC. Degree of conversion (n = 40) was analyzed by using FT-Raman spectroscopy. A 3-point loading test was used to evaluate the flexural strength of the specimens (n = 80). One fragment of each flexural test specimen was then submitted to Vickers microhardness test.Results. WB produced a significant decrease (p