The cobalt(II) chloride N,N,N-pincer complexes, [2-{(2,4-(C15H13)2-6-FC6H2)N=CMe}-6-(ArN=CMe)C5H3N]CoCl2 (Ar = 2,6-Me2C6H3) (Co1), 2,6-Et2C6H3 (Co2), 2,6-i-Pr2C6H3 (Co3), 2,4,6-Me3C6H2 (Co4), 2,6-Et2-4-MeC6H2 (Co5), and [2,6-{(2,4-(C15H13)2-6-FC6H2)N=CMe}2C5H3N]CoCl2 (Co6), each containing at least one N-2,4-bis(dibenzosuberyl)-6-fluorophenyl group, were synthesized in good yield from their corresponding unsymmetrical (L1–L5) and symmetrical bis(imino)pyridines (L6). The molecular structures of Co1 and Co2 spotlighted their distorted square pyramidal geometries (τ5 value range: 0.23–0.29) and variations in steric hindrance offered by the dissimilar N-aryl groups. On activation with either MAO or MMAO, Co1–Co6 all displayed high activities for ethylene polymerization, with levels falling in the order: Co1 > Co4 > Co5 > Co2 > Co3 > Co6. Indeed, the least sterically hindered 2,6-dimethyl Co1 in combination with MAO exhibited a very high activity of 1.15 × 107 g PE mol−1 (Co) h−1 at the operating temperature of 70 °C, which dropped by only 15% at 80 °C and 43% at 90 °C. Vinyl-terminated polyethylenes of high linearity and narrow dispersity were generated by all catalysts, with the most sterically hindered, Co3 and Co6, producing the highest molecular weight polymers [Mw range: 30.26–33.90 kg mol−1 (Co3) and 42.90–43.92 kg mol−1 (Co6)]. In comparison with structurally related cobalt catalysts, it was evident that the presence of the N-2,4-bis(dibenzosuberyl)-6-fluorophenyl groups had a limited effect on catalytic activity but a marked effect on thermal stability.