This work describes the development of a new post-implant crystal recovery technique in 4H-SiC using XeCl (l=308 nm) multiple laser pulses in the ns regime. Characterization was carried out through micro-Raman spectroscopy, Photoluminescence (PL), Transmission Electron Microscopy (TEM) and outcomes were than compared with 1h thermally annealed at 1650-1770-1750 °C P implanted samples (source implant) and P and Al implanted samples for 30 minutes at 1650 °C (source and body implants). Experimental results demonstrate that laser annealing enables crystal recovery in the energy density range between 0.50 and 0.60 J/cm². Unlike the results obtained with thermal annealing where stress up to 172 Mpa and high carbon vacancies (V_c) concentration is recorded, laser annealing provides almost stress free samples and much less defective crystal avoiding intra-bandgap carrier recombination. Implant was almost preserved except for step-bouncing and surface oxidation phenomena leading to surface roughening. However, the results of this work gives way to laser annealing process practicability for lattice damage recovery and dopant activation.