Elsevier, Physica C: Superconductivity and its Applications, (372-376), p. 675-678
DOI: 10.1016/s0921-4534(02)00828-6
Full text: Unavailable
Thin films of the superconducting Nd1+xBa2−xCu3O7−δ (NBCO) and Y1(NdxBa2−x)Cu3O7−δ (YNBCO) compounds have been deposited by dc magnetron sputtering and diode high pressure oxygen sputtering. Different techniques, including scanning tunneling microscopy, atomic force microscopy, X-ray diffraction and transmission electron microscopy (TEM) have been used to study the film microstructures and the surface morphology. It is shown that the Nd/Ba exchange promotes a 2D heteroepitaxial growth in the case of the NBCO films deposited on (1 0 0) SrTiO3 substrates, with a suppression of the characteristic 3D spirals structures. On the contrary in YNBCO the Nd/Ba exchange does not provide a driving force for the suppression of screw-dislocations, since spirals or towers originated by screw and half loop dislocations are observed on the surface. TEM reveals that anti-phase boundaries are eliminated during the growth of NBCO films thanks to the Nd/Ba exchange while this mechanism is not operating in the case of YNBCO films.