Using in situ high-pressure Raman spectroscopy and X-ray diffraction, the polymerization and structure evaluation of C60 were studied up to 16 GPa at room temperature. The use of an 830 nm laser successfully eliminated the photo-polymerization of C60, which has interfered with the pressure effect in previous studies when a laser with a shorter wavelength was used as excitation. It was found that face-centered cubic (fcc) structured C60 transformed into simple cubic (sc) C60 due to the hint of free rotation for the C60 at 0.3 GPa. The pressure-induced dimerization of C60 was found to occur at about 3.2 GPa at room temperature. Our results suggest the benefit and importance of the choice of the infrared laser as the excitation laser.