Elsevier, Physica B: Condensed Matter, 1-2(397), p. 65-67
DOI: 10.1016/j.physb.2007.02.066
Full text: Download
Polarized neutron reflectivity (PNR) studies have been performed on granular multilayers [Co80Fe20(tn)/Al2O3(3nm)]m. For a non-percolating superferromagnetic sample (tn = 1.3 nm) no spin-flip scattering was observed, measured at various points of the hysteresis, confirming that the magnetization reversal is achieved merely by domain nucleation and growth. For a percolated sample (tn = 1.6 nm) an oscillating magnetization depth profile from FeCo layer to FeCo layer along the multilayer stack was observed around the coercive field. The competition between long-range dipolar, short-range Néel and external field interactions apparently give rise to such a modulated magnetization depth profile in these magnetic multilayers.