American Chemical Society, ACS Applied Materials and Interfaces, 9(4), p. 4637-4642, 2012
DOI: 10.1021/am301012p
Full text: Download
We show the importance of sidewall chemistry for the graphoepitaxial alignment of PS-b-PDMS using prepatterns fabricated by electron beam lithography of hydrogen silsesquioxane (HSQ) and by deep ultraviolet (DUV) lithography on SiO(2) thin films. Density multiplication of polystyrene-block-polydimethylsiloxane (PS-b-PDMS) within both prepatterns was achieved by using a room temperature dynamic solvent annealing environment. Selective tuning of PS and PDMS wetting on the HSQ template sidewalls was also achieved through careful functionalization of the template and substrate surface using either brush or a self-assembled trimethylsilyl monolayer. PDMS selectively wets HSQ sidewalls treated with a brush layer of PDMS, whiereas PS is found to selectively wet HSQ sidewalls treated with hexamethyldisilazane (HMDS) to produce a trimethylsilyl-terminated surface. The etch resistance of the aligned polymer was also evaluated to understand the implications of using block copolymer patterns which have high etch resistance, self-forming (PDMS) wetting layers at both interfaces. The results outlined in this work may have direct applications in nanolithography for continued device scaling toward the end-of-roadmap era.