Mechanism of Early Stage Corrosion for Boric-sulfuric Acid Anodized 2A97 Al-Cu-Li Alloy Under Tropical Marine Atmosphere

This paper is available in a repository.
This paper is available in a repository.

Full text: Download

Question mark in circle
Preprint: policy unknown
Question mark in circle
Postprint: policy unknown
Question mark in circle
Published version: policy unknown

Abstract

Optical microscopy(OM), scanning electron microscopy(SEM), EDX and EIS combined with ultramicrotomy were employed to investigate the micro morphology, chemical composition and electrochemical properties of anodized 2A97 Al-Cu-Li alloy before and after atmospheric corrosion. The results show that when electrolytes containing combinations of tartaric-sulfuric or boric-sulfuric acid are used to grow the films at different temperatures, boric acid addition and higher temperature allow for higher current density that speeds up the film growth. The pore geometry and structure is similar for different electrolytes. Dispersive dark rusty spots composed of O, Al, Cl, Cu are present on the boric-sulfuric acid anodized specimen after exposure in tropical marine atmosphere for 1 month. Deposition of white corrosion product is found on the specimen surface as well. Severe pitting occurs and develops deeply into the alloy substrate after elongated outdoor exposure. Corrosion propagation is associated with θ -phase particles.