Solid-state polycondensation of Poly(ethylene terephthalate) films

This paper is available in a repository.
This paper is available in a repository.

Full text: Download

Question mark in circle
Preprint: policy unknown
Question mark in circle
Postprint: policy unknown
Question mark in circle
Published version: policy unknown

Abstract

The solid-state polycondensation of poly(ethylene terephthalate) (PET) amorphous and unoriented films from Du Pont (precursor for their Mylar® 1 polyester film) prepared from a specified catalyst and monomer system has been studied. The effect of various reaction parameters such as reaction temperature and time on inherent viscosity (ηinh) and number of carboxy and hydroxy end-groups has been investigated. From ηinh measurements an empirical equation was taken which allows the calculation of (M̄n) of PET film after solid-state polycondensation at a certain temperature and time. The melting behaviour of the solid-state polycondensated samples was also studied.Die Festphasen-Polykondensation von amorphen, unorientierten Poly(ethylenterephthalat)-Folien (PET) (Vorstufe der Du Pont Mylar®1 -Polyesterfilme), die mit einem speziellen Katalysator-und Monomer-System hergestellt wurden, war Gegenstand dieser Arbeit. Der Einfluß verschiedener Reaktionsparameter, wie Reaktionstemperatur und -zeit, auf die inhärente Viskosität (ηinh) und auf die Anzahl der Carboxy-und Hydroxy-Endgruppen wurde untersucht. Aus den Messungen von ηinh wurde eine empirische Gleichung erstellt, die die Berechnung von M̄n der PET-Folien nach der Festphasen-Polykondensation bei gegebener Zeit und Temperatur erlaubt. Das Schmelzverhalten verschiedener Festphasen-Polykondensate wurde ebenfalls untersucht.