We report on an IR spectroscopic study on the room-temperature adsorption of NO on different iron(II)-containing siliceous matrices. Fe2+ hosted inside the channels of MFI-type zeolites (Fe-ZSM-5 and Al-free Fe-silicalite) exhibits pronounced coordinative unsaturation, as witnessed by the capability to form, at 300 K, [Fe2+(NO)], [Fe2+(NO)(2)] and [Fe2+(NO)(3)] complexes with increasing NO equilibrium pressure. Fe2+ hosted on amorphous supports (high surface area SiO2 and MCM-41) sinks more deeply into the surface of the siliceous support and thus exhibits less pronounced coordinative unsaturation only [Fe2+(NO)(2)] complexes were observed, even at the highest investigated NO equilibrium pressures. Activation at higher temperature (1073 K) of the Al-free Fe-silicalite sample resulted in the appearance of Fe2+ species similar to those observed on SiO2 and MCM-41, and this suggests that local (since not detectable by X-ray diffraction) amorphisation of the environment around Fe2+ anchoring sites occurs. The fact that this behaviour is not observed on the Fe-ZSM-5 sample activated at the same temperature suggests that framework Al species (and their negatively charged oxygen environment) have an important role in anchoring extraframework Fe2+ species. Such an anchoring phenomenon will prevent a random migration of iron species, with subsequent aggregation and loss of coordinative unsaturation. These observation can thus explain the higher catalytic activity of the Fe-ZSM-5 system in one-step benzene to phenol conversion when compared with the parent, Al-free, Fe-silicalite system with similar Fe content. The nature of the support and the activation temperature can therefore be used as effective means to tune the degree of Fe coordination.